€560.00 – €1,350.00 exVAT

Honeycomb Core Sandwich Panels consist of two 0.5mm or 1.0mm carbon fibre skins that ‘sandwich’ an Aluminium Honeycomb Core 1/4inch (6.4mm) cell size 5.2-1/4-25N-3003  core. The surface finish of both skins is smooth and glossy as standard although a matte bonding surface can be specified if desired.

Lead time: Contact us (Made to order – approximately 15 working days)

Clear

SKU N/A Category

Share

HONEYCOMB SANDWICH PANELS

Carbonfibreshop.com supply a range of advanced composite honeycomb core sandwich panels. Skins can consist of carbon, glass or basalt fibre with aluminum or aramid honeycomb cores.
Common specifications are available to order online however, please get in touch to discuss your requirements such as: thickness, size, quantity, core type and skin type.
Carbon Fibre Sandwich Panels consist of two 0.5mm or 1.0mm carbon fibre skins that ‘sandwich’ an Aluminium Honeycomb Core 1/4inch (6.4mm) cell size 5.2-1/4-25N-3003  core.
Glass Fibre Sandwich Panels consist of two 0.5mm or 1.0mm carbon fibre skins that ‘sandwich’ an Aluminium Honeycomb Core 19.1mm (3/4“) cell size honeycomb cell size 5.2-1/4-25N-3003  core.
The surface finish of both skins is smooth and glossy as standard although a matte bonding surface can be specified if desired.
Customised sandwich core panel constructions are possible e.g. core type, core density, skin materials, temperature performance and surface finish – please use the contact form to get more details.
Other key features of our carbon fibre foam core sandwich panels  include: consistent high quality, excellent adhesion/peel strength between carbon fibre skins and foam core, excellent chemical resistance, low water absorption and good thermal/acoustic insulation.
Our carbon fibre sandwich core panels are amongst the most valued composite manufacturing innovations that have been developed  within the industry, which have found multi-sectoral application such as aerospace, automotive, mass transportation, marine and industrial automation.

The key benefits of our sandwich carbon fibre sandwich core panels

– Very low weight

– High stiffness

– Durability

– Cosmetic finish

Properties of Composite Sandwich Panels With Core

Unit of Measure

Test Method

6mm

11mm

21mm

Long Beam Bending

Pmax

Deflection at 445N (100lb)

N (lb)

mm (inch)

MIL-STD-401B*

435 (98)

N/A

1100 (247)

10.9 (0.43)

2000 (450)

3.45 (0.14)

Flexural Strength Skin

MPa (ksi)

ASTM D7264/D7264M (Procedure A)

820

(119)

820

(119)

820

(119)

Flexural Modulus Skin

GPa (psi)

ASTM D7264/D7264M (Procedure A)

60

(8702)

60

(8702)

60

(8702)

Core Density

kg/m3

60

60

60

Areal Weight (skins & core)

[mass of 2440x1220mm panel]

kg/m2

[kg]

  2.95

[8.8]

  4.06

[12.1]

4.80

[14.1]

Max operating temp

OC (F)

DMA (onset of E)

85 (194)

85 (194)

85 (194)

*ASTM C393-00 using 20inch span Quarter Point loading arrangement

Our sandwich core panels can be supplied with a smooth glossy (non UV stable) surface or a textured matte bonding surface. A high gloss UV stable finish can be achieved with sanding and finishing with a good quality automotive 2K Epoxy-Urethanes, Polyurethanes or Acrylic Spray Lacquers

Additional information
Dimensions N/A
SANDWICH Thickness

13.7 mm, 14.7 mm
Dimensions

1220×1200, 2440×1200